The Significance of Oxide Layers in Boundary Lubrication

[+] Author and Article Information
K. Komvopoulos, N. Saka, N. P. Suh

Department of Mechanical Engineering, Massachusetts Institute of Technology, Cambridge, Mass. 02139

J. Tribol 108(4), 502-513 (Oct 01, 1986) (12 pages) doi:10.1115/1.3261253 History: Received August 15, 1985; Online October 29, 2009

Abstract

Analytical and experimental studies were conducted on oxidized and nonoxidized pure aluminum, OFHC copper, and electroplated chromium to investigate the role of surface oxide layers in boundary lubrication. The effects of the thickness of the oxide layers, the elastic moduli of the oxide and the metal, and the normal surface traction have been addressed. In addition, several possible failure mechanisms of both thin and thick oxide films have been proposed. The experimental results have shown that low coefficients of friction, about 0.1 or less, and especially low wear can be obtained in boundary-lubricated sliding if the metal surfaces are protected from plastic deformation by sufficiently thick oxide layers. Scanning electron microscopy has shown that when the oxide layers are not ruptured, the wear of the surfaces is negligibly small. In this case, the oxide-oxide contacts deform primarily elastically and the predominant friction mechanism is the shear of the lubricant film. Based on this evidence, a theoretical model for friction was proposed and the agreement between theoretical and experimental coefficients of friction was reasonably good. Disruption of the oxide layers during sliding, however, was found to result in plastic deformation and plowing of the surfaces.

Copyright © 1986 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In