Mechanism of Mild to Severe Wear Transition in Alpha-Alumina

[+] Author and Article Information
S. Jahanmir, X. Dong

Tribology Group, National Institute of Standards and Technology, Gaithersburg, MD 20899

J. Tribol 114(3), 403-411 (Jul 01, 1992) (9 pages) doi:10.1115/1.2920899 History: Received November 27, 1990; Revised May 01, 1991; Online June 05, 2008


Friction and wear experiments were conducted on high purity alpha-alumina sliding against a similar material in air under different contact loads and at temperatures ranging from 23°C to 900°C. Experimental results indicate that tribochemical reactions between water vapor and alpha-alumina at room temperature produce aluminum hydroxide which results in relatively low coefficients of friction and low wear rates. Both the coefficient of friction and the wear rate of alumina were low at intermediate temperatures (200°C to 800°C), if the contact stress was below a threshold value. Above this load, wear occurred by fracture, the wear coefficient exceeded a value of 10−4 , and the coefficient of friction increased to 0.90. At 900°C, the coefficient of friction was 0.40 and the wear coefficient was reduced to a value less than 10−6 , because of the formation of a silicon-rich layer on the wear track. A contact mechanics model based on linear elastic fracture mechanics indicated that propagation of cracks from pre-existing flaws controls the onset of catastrophic wear in the intermediate temperature range.

Copyright © 1992 by The American Society of Mechanical Engineers
Your Session has timed out. Please sign back in to continue.






Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In