Depth of Penetration as a Predictor of the Wear Polymers on Hard, Rough Surfaces

[+] Author and Article Information
J. H. Warren, N. S. Eiss

Virginia Polytechnic Institute and State University, Blacksburg, Va.

J. of Lubrication Tech 100(1), 92-97 (Jan 01, 1978) (6 pages) doi:10.1115/1.3453123 History: Received January 18, 1977; Online October 20, 2010

Abstract

Polymers were slid on rough, hard surfaces with normal loads which caused full penetration (real and apparent areas equal) and partial penetration (real less than apparent area). SEM photographs of full penetration showed that the polymer sheared off at an angle to the horizontal, the shear angles were 10.8, 12.6, and 18.9 deg for polyvinylchloride, polychlorotrifluoroethylene, and nylon 6/6, respectively. These shear angles correlated with the energy-to-rupture of the polymers and inversely with the wear of polyvinyl-chloride and polychlorotrifluoroethylene. In partial penetration experiments the wear of polyvinylchloride and polychlorotrifluoroethylene could be discriminated by the depth of penetration of the surface into the polymer. The penetration depth is a function of the polymer yield strength and the bearing area curve of the surface.

Copyright © 1978 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In