Three-Dimensional Molecular Dynamics Analysis of Atomic-Scale Indentation

[+] Author and Article Information
W. Yan, K. Komvopoulos

Department of Mechanical Engineering, University of California, Berkeley, CA 94720

J. Tribol 120(2), 385-392 (Apr 01, 1998) (8 pages) doi:10.1115/1.2834438 History: Received November 09, 1996; Revised June 10, 1997; Online January 24, 2008

Abstract

The complete atomic-scale indentation cycle is analyzed using molecular dynamics simulations. A hysteresis is observed in the instantaneous normal force versus surface separation distance curve obtained with an atom or a rigid tip indenting and, subsequently, retracting from a dynamic face-centered-cubic substrate consisting of argon or copper. The generation of irreversible deformation in a Lennard-Jones solid is revealed in light of simulation results for indentation by a single atom. The direction of irreversible deformation is shown to coincide with that of macroscopic plastic flow. The compressive yield strength decreases with increasing substrate temperature and decreasing indentation speed. The phenomena of tip wetting by substrate atoms and connective neck formation, elongation, and rupture at the tip/substrate interface are elucidated by simulation results for the unloading process. It is shown that energy dissipation decreases as the substrate temperature increases and the energy consumed by irreversible deformation is always greater than that due to heating.

Copyright © 1998 by The American Society of Mechanical Engineers
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In