Research Papers: Lubricants

Tribological Improvements of Dispersed Nanodiamond Additives in Lubricating Mineral Oil

[+] Author and Article Information
Matthew Marko

Navy Air Warfare Center Aircraft Division,
JB-MDL, Highway 547,
Lakehurst, NJ 08733
Department of Mechanical Engineering,
Columbia University,
500 W 120 Street,
New York, NY 10027
e-mail: matthew.marko@navy.mil

Jonathan Kyle

Department of Mechanical Engineering,
Columbia University,
500 W 120 Street,
New York, NY 10027
e-mail: jpk2128@columbia.edu

Blake Branson

sp3 Nanotech, LLC,
1448 Halsey Way, Suite 110,
Carrollton, TX 75007
e-mail: blake_branson@sp3nanotech.com

Elon Terrell

Department of Mechanical Engineering,
Columbia University,
500 W 120 Street,
New York, NY 10027
e-mail: eterrell@columbia.edu

1Corresponding author.

Contributed by the Tribology Division of ASME for publication in the JOURNAL OF TRIBOLOGY. Manuscript received April 8, 2014; final manuscript received July 21, 2014; published online October 21, 2014. Assoc. Editor: George K. Nikas.

This work is in part a work of the U.S. Government. ASME disclaims all interest in the U.S. Government's Contributions.

J. Tribol 137(1), 011802 (Oct 21, 2014) (7 pages) Paper No: TRIB-14-1077; doi: 10.1115/1.4028554 History: Received April 08, 2014; Revised July 21, 2014

An effort was conducted to study and characterize the effects of nanodiamond particles as an additive to lubricating mineral oil. The tests were run for varying concentrations ranging from pure mineral oil to 0.01% weight-concentration of nanodiamonds. The friction was measured throughout the tests, and the resulting wear was measured with optical profilometry. It was observed that both the average friction coefficient and the wear would decrease proportionally to the concentration of nanodiamond particles, and the 0.01% nanodiamond weight concentration was observed to improve the tribological performance of lubricating mineral oil. Chemical analysis of contacting surfaces showed no significant distinction from the nanodiamond mixture versus the pure mineral oil, while particle size analysis demonstrated that the nanoparticles themselves remained intact (i.e., no breakup) in the contact interface. This helps to conclude that a mechanical and not a chemical effect of the nanodiamond particles helped to protect the metallic surface from wear and improve the lubricating ability of the mineral oil.

Copyright © 2015 by ASME
Your Session has timed out. Please sign back in to continue.


Tao, X., Jiazheng, Z., and Kang, X., 1996, “The Ball-Bearing Effect of Diamond Nanoparticles as an Oil Additive,” J. Phys. D: Appl. Phys., 29(11), pp. 2932–2937. [CrossRef]
Mochalin, V., Shenderova, O., Ho, D., and Gogotsi, Y., 2012, “The Properties and Applications of Nanodiamonds,” Nat. Nanotechnol., 7(1), pp. 11–23. [CrossRef]
Wu, Y., Tsui, W., and Liu, T., 2007, “Experimental Analysis of Tribological Properties of Lubricating Oils With Nanoparticle Additives,” Wear, 262(7–8), pp. 819–825. [CrossRef]
Padgurskas, J., Rukuiza, R., Prosycevas, I., and Kreivaitis, R., 2013, “Tribological Properties of Lubricant Additives of Fe, Cu and Co Nanoparticles,” Tribol. Int., 60, pp. 224–232. [CrossRef]
Sunqing, Q., Junxiu, D., and Guoxu, C., 2000, “Wear and Friction Behaviour of CaCO3, Nanoparticles Used as Additives in Lubricating Oils,” Lubr. Sci., 12(2), pp. 205–212. [CrossRef]
Rapoport, L., Leshchinsky, V., Lapsker, I., Volovik, Y., Nepomnyashchy, O., Lvovsky, M., Popovitz-Biro, R., Feldman, Y., and Tenne, R., 2003, “Tribological Properties of WS2 Nanoparticles Under Mixed Lubrication,” Wear, 255(7–12), pp. 785–793. [CrossRef]
Reeves, C., Menezes, P., Lovell, M., and Jen, T., 2013, “The Size Effect of Boron Nitride Particles on the Tribological Performance of Biolubricants for Energy Conservation and Sustainability,” Tribol. Lett., 51(3), pp. 437–452. [CrossRef]
Pawlak, Z., Kaldonski, T., Pai, R., Bayraktar, E., and Oloyede, A., 2009, “A Comparative Study on the Tribological Behaviour of Hexagonal Boron Nitride (H–BN) as Lubricating Micro-Particles—An Additive in Porous Sliding Bearings for a Car Clutch,” Wear, 267(5–8), pp. 1198–1202. [CrossRef]
Zhou, J., Wu, Z., Zhang, Z., Liu, W., and Dang, H., 2001, “Study on an Antiwear and Extreme Pressure Additive of Surface Coated LaF3 Nanoparticles in Liquid Paraffin,” Wear, 249(5–6), pp. 333–337. [CrossRef]
Chen, S., Liu, W., and Yu, L., 1998, “Preparation of DDP-Coated PbS Nanoparticles and Investigation of the Antiwear Ability of the Prepared Nanoparticles as Additive in Liquid Paraffin,” Wear, 218(2), pp. 153–158. [CrossRef]
Chen, S., and Liu, W., 2006, “Oleic Acid Capped PbS Nanoparticles: Synthesis, Characterization and Tribological Properties,” Mater. Chem. Phys., 98(1), pp. 183–189. [CrossRef]
Liu, W., and Chen, S., 2000, “An Investigation of the Tribological Behaviour of Surface-Modified ZnS Nanoparticles in Liquid Paraffin,” Wear, 238(2), pp. 120–124. [CrossRef]
Xue, Q., Liu, W., and Zhang, Z., 1997, “Friction and Wear Properties of a Surface-Modified TiO2 Nanoparticle as an Additive in Liquid Paraffin,” Wear, 213(1–2), pp. 29–32. [CrossRef]
Hu, Z., and Dong, J., 1998, “Study on Antiwear and Reducing Friction Additive of Nanometer Titanium Oxide,” Wear, 216(1), pp. 92–96. [CrossRef]
Volovik, Y., and Tenne, R., 2002, “Friction and Wear of Powdered Composites Impregnated With WS2 Inorganic Fullerene-Like Nanoparticles,” Wear, 252(5–6), pp. 518–527. [CrossRef]
Rapoport, L., Leshchinsky, V., Lvovsky, M., Lapsker, I., Volovik, Y., Feldman, Y., Popovitz-Biro, R., and Tenne, R., 2003, “Superior Tribological Properties of Powder Materials With Solid Lubricant Nanoparticles,” Wear, 255(7–12), pp. 794–800. [CrossRef]
Rapoport, L., Feldman, Y., Homyonfer, M., Cohen, H., Sloan, J., Hutchison, J., and Tenne, R., 1999, “Inorganic Fullerene-Like Material as Additives to Lubricants: Structure–Function Relationship,” Wear, 225–229(Part 2), pp. 975–982. [CrossRef]
Rapoport, L., Nepomnyashchy, O., Lapsker, I., Verdyan, A., Moshkovich, A., Feldman, Y., and Tenne, R., 2005, “Behavior of Fullerene-Like WS2 Nanoparticles Under Severe Contact Conditions,” Wear, 259(1–6), pp. 703–707. [CrossRef]
Maharaj, D., and Bhushan, B., 2013, “Effect of Mo2 and WS2 Nanotubes on Nanofriction and Wear Reduction in Dry and Liquid Environments,” Tribol. Lett., 49(2), pp. 323–339. [CrossRef]
American Society for Testing and Materials (ASTM) D-4172, 1994, Standard Test Method for Wear Preventive Characteristics of Lubricating Fluid, ASTM, Materials Park, OH.
Erdemir, A., and Donnet, C., 2006, “Tribology of Diamond-Like Carbon Films: Recent Progress and Future Prospects,” J. Phys. D: Appl. Phys., 39(18), pp. 311–327. [CrossRef]
Gupta, B., Malshe, A., Bhushan, B., and Subramaniam, V., 1994, “Friction and Wear Properties of Chemomechanically Polished Diamond Films,” ASME J. Tribol., 116(3), pp. 445–453. [CrossRef]
Grierson, D. S., Sumant, A. V., Konicek, A. R., Friedmann, T. A., Sullivan, J. P., and Carpick, R. W., 2010, “Thermal Stability and Rehybridization of Carbon Bonding in Tetrahedral Amorphous Carbon,” J. Appl. Phys., 107(3), p. 033523. [CrossRef]
Konicek, A., Grierson, D., Gilbert, P., Sawyer, W., Sumant, A., and Carpick, R., 2008, “Origin of Ultralow Friction and Wear in Ultrananocrystalline Diamond,” Phys. Rev. Lett., 100(23), p. 235502. [CrossRef] [PubMed]
Siegbahn, K., and Edvarson, K., 1956, “β-Ray Spectroscopy in the Precision Range of 1:105,” Nucl. Phys., 1(8), pp. 137–159. [CrossRef]
Wanga, S., Zhanga, Q., Yoona, S., Ahna, J., Zhoua, Q., Wang, Q., Yanga, D., Lia, J., and Shanyongb, S., 2003, “Electron Field Emission Enhancement Effects of Nano-Diamond Films,” Surf. Coat. Technol., 167(2–3), pp. 143–147. [CrossRef]
Xu, T., Yang, S., Chen, M., Tian, J., Xue, Q., Li, J., and Guo, W., 2002, “Influence of Nitrogen Ion Implantation on Tribological Properties of Nanocrystalline Diamond Films,” J. Phys. D: Appl. Phys., 35(8), pp. 788–793. [CrossRef]
Osswald, S., Yushin, G., Mochalin, V., Kucheyev, S., and Gogotsi, Y., 2006, “Control of sp2/sp3 Carbon Ratio and Surface Chemistry of Nanodiamond Powders by Selective Oxidation in Air,” J. Am. Chem. Soc., 128(35), pp. 11635–11642. [CrossRef] [PubMed]
Branson, B., Seif, M., Davidson, J., and Lukehart, C., 2011, “Fabrication and Macro/Nanoscale Characterization of Aggregated and Highly De-Aggregated Nanodiamond/Polyacrylonitrile Composite Thick Films,” J. Mater. Chem., 21(46), pp. 18832–18839. [CrossRef]
Goldburg, W. I., 1999, “Dynamic Light Scattering,” Am. J. Phys., 67(12), pp. 1152–1160. [CrossRef]
Schatzel, K., Drewel, M., and Ahrens, J., 1990, “Suppression of Multiple Scattering in Photon Correlation Spectroscopy,” J. Phys.: Condens. Matter, 2(Suppl.), pp. SA393–SA398. [CrossRef]
Segrè, P., Megen, W. V., Pusey, P., Schätzel, K., and Peters, W., 1995, “Two-Colour Dynamic Light Scattering,” J. Mod. Opt., 42(9), pp. 1929–1952. [CrossRef]
Shakhvorostov, D., Müser, M., Song, Y., and Norton, P., 2009, “Smart Materials Behavior in Phosphates: Role of Hydroxyl Groups and Relevance to Antiwear Films,” J. Chem. Phys., 131(4), p. 044704. [CrossRef] [PubMed]
Blau, P., 2005, “On the Nature of Running-In,” Tribol. Int., 38(11–12), pp. 1007–1012. [CrossRef]
Repoux, M., 1992, “Comparison of Background Removal Methods for XPS,” Surf. Interface Anal., 18(7), pp. 567–570. [CrossRef]
Diaz, J., Paolicelli, G., Ferrer, S., and Comin, F., 1996, “Separation of the sp2 and sp3 Components in the C 1s Photoemission Spectra of Amorphous Carbon Films,” Phys. Rev. B, 54(11), pp. 8064–8069. [CrossRef]
Haerle, R., Riedo, E., Pasquarello, A., and Baldereschi1, A., 2001, “sp2/sp3 Hybridization Ratio in Amorphous Carbon From C 1s Core-Level Shifts: X-Ray Photoelectron Spectroscopy and First-Principles Calculation,” Phys. Rev. B, 65(4), p. 045101. [CrossRef]


Grahic Jump Location
Fig. 3

Experimental measurements of viscosity as a function of temperature, for (a) mineral oil and (b) 0.01% nanodiamond weight concentration

Grahic Jump Location
Fig. 2

DLS results for the nanodiamond particle diameter, both before and after a four-ball test. The DLS measurement determined both the deflection angle as well as the spectral absorption for a light propagating through the nanodiamond solution.

Grahic Jump Location
Fig. 1

TEM images of 60 nm slices of nanocomposites with (a) UDD filler and (b) nanodiamond filler. (c) TEM image of 40 nm microtome of the vinyl ester composite filled with 3.5% weight concentration nanodiamond–vinyltrimethoxysilane (VTMS).

Grahic Jump Location
Fig. 4

Time resolved measured COF throughout four-ball test, lubricated with (a) mineral oil, (b) mineral oil with 0.0025% nanodiamond weight concentration, and (c) mineral oil with 0.01% nanodiamond weight concentration. Repeat tests are shown.

Grahic Jump Location
Fig. 5

Experimentally measured COF as a function of nanodiamond weight concentration

Grahic Jump Location
Fig. 6

FTIR spectra of (a) straight nanodiamond as received from the manufacturer, (b) surface-functionalized nanodiamond during additive synthesis, (c) mineral oil without nanodiamond additive after four-ball testing, and (d) mineral oil containing dispersed nanodiamond particles after four-ball testing

Grahic Jump Location
Fig. 7

Calculated peak from high-analysis study near the excitation energy of carbon. Study includes both the wear scar after a mineral oil four-ball test (bottom) and the wear scar after the nanodiamond four-ball test (top). The peaks were solved with the Shirley background function.

Grahic Jump Location
Fig. 8

Results of the Zygo profile-meter after a 0.01% weight concentration nanodiamond four-ball test, including: (a) the microscopic image of the wear scar, and (b) the 3D measured profile; X and Y labels are in mm, grayscale bar represents micrometers of wear

Grahic Jump Location
Fig. 9

Measured profiles of wear scars, for (a) 0.01% nanodiamond weight concentration, (b) 0.0025% nanodiamond weight concentration, and (c) mineral oil

Grahic Jump Location
Fig. 10

Measured wear volume as a function of nanodiamond weight concentration

Grahic Jump Location
Fig. 11

RMS surface roughness of wear scars. Clear bars represent average roughness, whereas error bars represent standard deviation of roughness, as a function of nanodiamond weight concentration.



Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In